Farget porselen
1 kg.
Bildet kun til illustrasjon, se brennprøver på verkstedet for sammenligning.
Denne typen leire resirkulerer vi ikke, det må du gjøre selv.
Obs: det er uvist hvordan leiren reagerer med våre dyppeglasurer.
Prisen inkluderer glasur, underglasur, voks, oxider og brenning.
Porselen- farget PORSELEN BLACK ICE
velg nummer
Størrelse
1 kg
Blue porcelain
Upsala is a unique blue porcelain noted for its beautiful cobalt blue. It has high plasticity, which makes it ideal for wheel-throwing and modelling. Its formula is very stable and provides a secure firing range between 1200 and 1240ºC (oxidizing atmosphere). Suitable for tableware (food-safe), according to ISO 6486. Available in extruded body (moist form). Presented in a practical 5 kg cylindrical format with double packaging.
Firing range: 1200-1240ºC
Biscuit temperature: 1000ºC
Water content: 21%
Plasticity (IP Atterberg): 11
Carbonate content (CaCO3): 0%
Drying shrinkage: 5.2%
Firing shrinkage (1220ºC): 10.4%
Porosity (water absorption at 1220ºC): 0.0%
Dry bending strength: 3.3 N/mm2
Fired bending strength (1220ºC): 47.2 N/mm2
Thermal coefficient (25-500ºC): 58.3x10^-7ºC^-1
Black porcelain
Black Ice is a black porcelain noted for its beautiful black graphite. It has high plasticity, which makes it ideal for wheel-throwing and modelling. Its formula is very stable and provides a secure firing range between 1200 and 1240ºC (oxidizing atmosphere). Suitable for tableware (food-safe), according to ISO 6486. Available in extruded body (moist form).
Firing range: 1200-1240ºC
Biscuit temperature: 1000ºC
Water content: 20%
Plasticity (IP Atterberg): 11
Carbonate content (CaCO3): 0%
Drying shrinkage: 5.4%
Firing shrinkage (1220ºC): 10.3%
Porosity (water absorption at 1220ºC): 0.0%
Dry bending strength: 3.1 N/mm2
Fired bending strength (1220ºC): 39.8 N/mm2
Thermal coefficient (25-500ºC): 54.3x10^-7ºC^-1